I would b tempted 2 anneal all that welding . Lot of stress been put in the tubes now .

snoopy72:
 :welcome
--- Quote from: animal on June 16, 2014, 05:57 PM ---I would b tempted 2 anneal all that welding . Lot of stress been put in the tubes now .

--- End quote ---
Shoundn't do Animal, TIG is a more controlled than MIG and I didn't cool it, all cooled down oh naturale,
If I had dunked it in water afterwards it would cause the metal to go brittle that's for sure.
 Thanks for the heads up, i'll will look into it  :daumenhoch:
What I did notice is when I held all the parts in the correct position while he tacked them they didn't even get luke warm , if it was MIG it would have cooked my pinkies.